SWD8030 two component polyaspartic top coating
Product features and advantages
* The coating film is tough, dense, full and bright with bright colors
* No discoloration, no yellowing, no pulverization, anti-aging, excellent weather resistance, light and color retention decoration performance
* Excellent adhesive strength, good compatibility with polyurethane, epoxy, chlorinated rubber, alkyd, phenolic and other coatings
*Excellent wear and impact resistance
*Excellent chemical resistance, such as acid, alkali, salt, etc
*Excellent corrosion resistance
*Excellent waterproof performance
*Excellent durability reduces maintenance costs
*Prolong the service life of spraying structure
Application scopes
All kinds of concrete, all kinds of metal structure surface anti-corrosion protection decoration.
Product information
| Item | Part A | Part B |
| appearance | Light yellow liquid | Color adjustable |
| specific gravity (g/m³) | 1.02 | 1.32 |
| Viscosity (cps) @25℃ | 230 | 210 |
| solid content (%) | 52 | 84 |
| Mixing ratio ( by weight) | 1 | 2 |
| surface dry time (h) | 1-2 h | |
| Coating interval (h) | Min 2h; Max 24 h（20℃） | |
| Theoretical coating rate (surface dry film thickness) | 0.10kg/㎡DFT 60μm | |
physical properties
| Item | Testing standard | results |
| Adhesive force | GB/T 6742-2007 | ≥2.5Mpa |
| Bending resistance | GB/T 6742-2007 | 1mm |
| abrasion resistance(750g/500r) mg | HG/T 3831-2006 | 5 |
| impact resistance kg·cm | GB/T 1732 | 50 |
| Weather resistance, Artificial accelerated aging,1000h | GB/T14522-1993 | color loss＜1, pulverization＜1 |
Chemical resistance
| Acid resistance 10%H2SO4 or 10%HCI,240h | No rust, no bubbles, no peel off |
| Alkali resistance 5% NaOH, 240h | No rust, no bubbles, no peel off |
| Salt resistance 30g/L,240h | No rust, no bubbles, no peel off |
| Salt spray resistance, 1500h | No rust, no bubbles, no peel off |
| Oil resistance 0# diesel, crude, 30d | No rust, no bubbles, no peel off |
| Water resistance 48H | No bubbles, wrinkling, discoloration or falling off |
| (For reference: Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data) | |
Application environment
| Environment temperature | -5~+35℃ |
| Relative humidity | ≤85% |
| Dew point | ≥3℃ |
Application tips
Brush, roller
Air spray, with air pressure 0.3-0.5Mpa
Airless spray, with spray pressure 15-20Mpa
Recommended dft: 30-60μm
Interval coating time: ≥3h
Application note
◆Agitate part B uniform prior to application
◆Mix well according to the requirements, pour out the same quantity based on the application, and use after mixing evenly.
◆After material pouring, the raw materials in the packaging barrel must be tightly covered to prevent moisture absorption
◆Keep dry and clean during the application, and do not contact with water, alcohol, acid, alkali, etc.
Curing time
| Substrate temperature | Surface dry time | Foot traffic | Solid dry |
| +10℃ | 2h | 8h | 7d |
| +20℃ | 1h | 6h | 5d |
| +30℃ | 1h | 4h | 3d |
Note: the curing time varies with the environment condition especially the temperature and relative humidity.
Shelf Life
* storage temperature: 5℃~35℃
* From the manufacturer date and on original package sealed condition:
Part A: 10 months
Part B: 10 months
Packing: Part A 25kg/drum, part B 25g/drum
Make sure the product package sealed well
* store in cool and ventilated place, avoid direct sunshine exposure.
Product health and safety information
For information and advice on the safe handling, storage and disposal of chemical products, users shall refer to the latest Material Safety Data Sheet containing physical, ecological, toxicological and other safety related data.
Integrity declaration
SWD guarantee all technical data stated in this sheet are based on laboratory tests. Actual testing methods may vary due to different circumstances. Therefore please test and verify its applicability. SWD does not take any other responsibilities except the product quality and reserve the right of any modifications on the listed data without prior notice.