Wholesale China Aliphatic Urethane Manufacturers – SWD8028 polyaspartic anticorrosion coating – SWD
Wholesale China Aliphatic Urethane Manufacturers – SWD8028 polyaspartic anticorrosion coating – SWD Detail:
Features and benefits
* high solids low density, with good leveling, the coating film is tough, dense, full light and bright colors
* excellent adhesive strength, good compatible with polyurethane, epoxy and other coating film.
* high hardness, good scratch resistance and stain resistance
* excellent abrasion resistance, impact resistance
* excellent anticorrosion property, resist to acid, alkali, salt and others.
* no discoloration, UV resistance, no yellowing, no powdering, aging resistance, with excellent weather resistance and gloss and color retention property
* can be applied directly to the surface of metal surface (DTM)
* this product is environmentally friendly and contains no benzene solvents and lead compounds
Product information
| Item | A component | B component |
| Appearance | light yellow liquid | Color adjustable |
| Specific gravity(g/m³) | 1.04 | 1.50 |
| Viscosity (cps)@25℃ | 40-60 | 100-200 |
| Solid content (%) | 58 | 90 |
| Mix ratio (by weight) | 1 | 1 |
| Surface dry time (h) | 1 | |
| Pot life (h)@25℃ | 1 | |
| Theoretical coverage (DFT) | 0.15kg/㎡ film thickness 100μm | |
Typical physical properties
| Item | Test standard | Results |
| Pencil hardness | H | |
| Adhesive strength（Mpa）metal base | HG/T 3831-2006 | 9.3 |
| Adhesive strength（Mpa）concrete base | HG/T 3831-2006 | 2.8 |
| Impermeability | 2.1Mpa | |
| Bending test (cylindrical shaft) | ≤1mm | |
| Abrasion resistance (750g/500r) mg | HG/T 3831-2006 | 5 |
| Impact resistance kg·cm | GB/T 1732 | 50 |
| Anti-aging, accelerated aging 1000h | GB/T14522-1993 | Loss of light＜1, chalking ＜1 |
Chemical resistance
| Acid resistance 40%H2SO4 or 10%HCI, 240h | no rust, no bubbles, no peel off |
| Alkali resistance 40%NaOH, 240h | no rust, no bubbles, no peel off |
| Salt resistance 60g/L, 240h | no rust, no bubbles, no peel off |
| Salt spray resistance 1000h | no rust, no bubbles, no peel off |
| Oil resistance, engine oil 240h | no rust, no bubbles, no peel off |
| Water resistance, 48h | No bubbles, no wrinkled,no color-changing, no peel off |
| (Note: The above chemical resistant property is obtained according to the GB/T9274-1988 test method, for reference only. Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data.) | |
Application instructions
Hand brush, roller
Air spray, with air pressure 0.3-0.5Mpa
Airless spray, with spray pressure 15-20Mpa
Recommend dft: 150-300μm
Recoating interval: min 1h, max 24h
Product cure time
| Substrate temperature | Surface dry time | Foot traffic | Solid dry time |
| +10℃ | 2h | 24h | 7d |
| +20℃ | 1.5h | 8h | 7d |
| +30℃ | 1h | 6h | 7d |
Note: the curing time is different with environment condition especially when temperature and relative humidity changes.
Shelf life
Storage temperature of environment: 5-35℃
* shelf life is from the manufacturing date and sealed condition
Part A: 10 months Part B: 10 months
* keep the package drum well sealed.
* store in cool and ventilated place, avoid sunshine exposure.
Package: part A: 25kg/barrel, part B: 25kg/barrel.
Product detail pictures:
Related Product Guide:
It adheres on the tenet "Honest, industrious, enterprising, innovative" to acquire new solutions continuously. It regards prospects, success as its personal success. Let us build prosperous future hand in hand for Wholesale China Aliphatic Urethane Manufacturers – SWD8028 polyaspartic anticorrosion coating – SWD , The product will supply to all over the world, such as: Slovenia, Johor, Riyadh, Our products are very popular in the word, like South American, Africa, Asia and so on. Companies to "create first-class products" as the goal, and strive to deliver customers with high quality solutions, present high-quality after-sales service and technical support, and customer mutual benefit, create a better career and future!
By Maggie from Hungary - 2017.12.02 14:11
The factory technical staff gave us a lot of good advice in the cooperation process, this is very good, we are very grateful.
By Cherry from Danish - 2017.10.23 10:29